PolyLite_ASA_TDS_V5.3.pdf
Innovators in 3D printing
Technical Data Sheet
PolyLite $ ^{ ext{TM}} $ ASA
PolyLite $ ^{ ext{TM}} $ ASA is an alternative to ABS with improved weather resistance. Its UV resistance and excellent mechanical properties make it the perfect choice for real-life applications.
PHYSICAL PROPERTIES
| Property | Testing Method | Typical Value |
|---|---|---|
| Density | ISO1183,GB/T1033 | 1.13g/cm³ at 23℃ |
| Melt index | 220℃, 10kg | 25g/10min |
| Light transmission | N/A | N/A |
| Flame retardancy | N/A | N/A |
| Property | Testing Method |
|---|---|
| Effect of weak acids | Resistant |
| Effect of strong acids | Slightly resistant |
| Effect of weak alkalis | Resistant |
| Effect of strong alkalis | Slightly resistant |
| Effect of organic solvent | Not resistant |
| Effect of oils and grease | Resistant |
MOISTURE ABSORPTION CURVE
THERMAL PROPERTIES
| Property | Testing Method | Typical Value |
|---|---|---|
| Glass transition temperature | DSC, 10℃/min | 97.8℃ |
| Melting temperature | DSC, 10℃/min | N/A |
| Crystallization temperature | DSC, 10℃/min | N/A |
| Decomposition temperature | TGA, 20℃/min | N/A |
| Vicat softening temperature | ISO306, GB/T1633 | 105.3℃ |
| Heat deflection temperature | ISO751, 8MPa | 100.2℃ |
| Heat deflection temperature | ISO750, 0.45MPa | 102.6℃ |
| Thermal conductivity | N/A | N/A |
| Heat shrinkage rate | N/A | N/A |
HDT CURVE
MECHANICAL PROPERTIES
| Property | Testing Method | Typical Value |
|---|---|---|
| Young's modulus (X-Y) | ISO 527, GB/T 1040 | 2174.6±41.1 MPa |
| Young's modulus (Z) | 1971.6±78.8 MPa | |
| Tensile strength (X-Y) | ISO 527, GB/T 1040 | 38.6±0.3 MPa |
| Tensile strength (Z) | 30.0±0.5 MPa | |
| Elongation at break (X-Y) | ISO 527, GB/T 1040 | 4.4±1.0% |
| Elongation at break (Z) | 2.4±0.1% | |
| Bending modulus (X-Y) | ISO 178, GB/T 9341 | 1939.7±50.4 MPa |
| Bending modulus (Z) | N/A | |
| Bending strength (X-Y) | ISO 178, GB/T 9341 | 60.9±0.9 MPa |
| Bending strength (Z) | N/A | |
| Charpy impact strength (X-Y) | ISO 179, GB/T 1043 | 10.5±0.6 kJ/m² |
RECOMMENDED PRINTING CONDITIONS
- Based on 0.4 mm nozzle and Simplify 3D v.4.0. Printing conditions may vary with different nozzle diameters.
| Parameter | |
|---|---|
| Nozzle temperature | 240-260 (℃) |
| Build surface material | BuildTak® |
| Build surface treatment | Magigoo |
| Build plate temperature | 75-95 (℃) |
| Cooling fan | OFF |
| Printing speed | 30-50 (mm/s) |
| Raft separation distance | 0.2 (mm) |
| Retraction distance | 1 (mm) |
| Retraction speed | 20 (mm/s) |
| Environmental temperature | Room temperature-90 (℃) |
| Threshold overhang angle | 50 (°) |
| Recommended support material | PolyDissolve™ S2 |
TENSILE TESTING SPECIMEN ISO 527, GB/T 1040
FLEXURAL TESTING SPECIMEN ISO 178, GB/T 9341
IMPACT TESTING SPECIMEN ISO 179, GB/T 1043
| Printing temperature | 260℃ |
|---|---|
| Bed temperature | 80℃ |
| Shell | 2 |
| Top & bottom layer | 4 |
| Infill | 100% |
| Environmental temperature | 70℃ |
| Cooling fan | OFF |
HOW TO MAKE SPECIMENS
DISCLAIMER:
The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End-use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.
Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/recycling practices of Polymaker materials for the intended application. Polymaker makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Polymaker shall not be made liable for any damage, injury, or loss induced from the use of Polymaker materials in any application.