HP 3D High Reusability PA 12
Strong, lowest cost,¹ quality parts
Produce strong, functional, detailed complex parts
- Robust thermoplastic produces high-density parts with balanced property profiles and strong structures.
- Provides excellent chemical resistance to oils, greases, aliphatic hydrocarbons, and alkalies.²
- Ideal for complex assemblies, housings, enclosures, and watertight applications.
- Biocompatibility certifications—meets USP Class I-VI and US FDA guidance for Intact Skin Surface Devices.³
Quality at the lowest cost per part¹
- Achieve the lowest cost per part¹ and reduce your total cost of ownership.⁴
- Minimize waste—reuse surplus powder batch after batch and get functional parts, no throwing away anymore.⁵
- Get consistent performance while achieving 80% surplus powder reusability.⁶
- Optimize cost and part quality—cost-efficient material with industry-leading surplus powder reusability.³
Engineered for HP Multi Jet Fusion technology
- Designed for production of functional parts across a variety of industries.
- Provides the best balance between performance and reusability.⁷
- Achieves watertight properties without any additional post-processing.
- Engineered to produce final parts and functional prototypes with fine detail and dimensional accuracy.
Technical specifications8
| Category | Measurement | Value | Method |
|---|---|---|---|
| General properties | Powder melting point (DSC) | 18℃/396°F | ASTM D13418 |
| Particle size | 60 µm | ASTM D13451 | |
| Bulk density of powder | 0.12 g/cm³/0.015 lb/in³ | ASTM D13468 | |
| Density of grains | 1.01 g/cm³/0.036 lb/in³ | ASTM D13792 | |
| Mechanical properties | Tensile strength, max load, X*Y | 48 Mpa/6960 psi | ASTM D638 |
| Tensile strength, max load, Z | 48 Mpa/6960 psi | ASTM D638 | |
| Tensile modulus, X*Y | 1800 MPa/261 kips | ASTM D638 | |
| Tensile modulus, Z | 1800 MPa/261 kips | ASTM D638 | |
| Elongation at break, X*Z | 20% | ASTM D638 | |
| Elongation at break, X*Z | 15% | ASTM D638 | |
| Flexural strength @ 5%, X*Y | 65% PMPa/250 psi | ASTM D1790 | |
| Flexural strength @ 5%, Z | 70% PMPa/250 psi | ASTM D1790 | |
| Flexural modulus, X*Y | 1730 PMPa/251 psi | ASTM D1790 | |
| Flexural modulus, Z | 1730 PMPa/251 psi | ASTM D1790 | |
| Lod impact notched @ 3.2 mm, 23°C), YX2 | 3.5 kJ/m² | ASTM D256 Test Method A | |
| Heat deflection temperature @ 0.45 MPa, 66 psi), XY | 175℃/347°F | ASTM D648 Test Method A | |
| Heat deflection temperature @ 1.82 MPa, 264 psi), XY | 95℃/203°F | ASTM D648 Test Method A | |
| Heat deflection temperature @ 1.82 MPa, 264 psi), Z | 95℃/203°F | ASTM D648 Test Method A | |
| Reusability | Refresh ratio for stable performance | 20% | |
| Recommended deuterium humidity | 50 %/70 %H | ||
| Certifications | GSP Class IV and US FDA guidance for Intact Skin Surface Devices, RoHS, EU REACH, PAHs, UL 94, UL 746A |
Ordering Information
| Product Name | Product Number | Weight | Capacity | Dimensions (xyz) | Compatibility |
|---|---|---|---|---|---|
| HP 30 High Reusability PA12 | V1R10A | 13 kg/28.7 lb | 301⁰ | 600 x 333 x 302 mm | HP Jet Fusion 410/420/420 |
| HP 30 High Reusability PA12 | V1R16A | 130 kg/286.7 lb | 3001⁰ | 800 x 600 x 325 mm | HP Jet Fusion 410/420/420 |
| HP 30 High Reusability PA12 | V1R34A | 130 kg/286.7 lb | 3001⁰ | 800 x 600 x 325 mm | HP Jet Fusion 410/420/420 |
| HP 30 High Reusability PA12 | V1R20A | 600 kg/1322.8 lb | 14001⁰ | 1143 x 1143 x 1500 mm | HP Jet Fusion 410/420/420 |
Eco Highlights
- Powders and agents are not classified as hazardous15
- Cleaner, more comfortable workplace—enclosed printing system, and automatic powder management
- Membranes used to indicate leading reusability of powder17
- Based on internal testing and safety data for solutions in market for last year, CNC cost analysis based on standard solution certification price, supplier price, and maintenance costs recommended by manufacturer.