TDS Crystal M2P CST VisiJet.pdf
ProJet® MJP 2500 Plus and VisiJet® M2P-CST Crystal
Jewelry Solution
Expand design freedom with 3D printed resin casting patterns that make possible ultra-fine features, thin walls, and lighter
weight jewelry
ProJet® MJP 2500 Plus and VisiJet® M2P-CST Crystal Jewelry Solution
Multiple 3D Printing technologies can be used for cost-effective jewelry production. The ProJet MJP 2500 Plus and VisiJet M2P-CST Crystal excel at producing resin casting patterns that possess intricate details, thin walls, and larger jewelry pieces that are lighter weight. This solution is ideal for high volume production that complements wax pattern printers where ultimate design flexibility is required, and the resolution and durability of fine features are critical considerations. Melt-away wax support structures maximize geometric freedom and aid in batch post-processing.
HIGHER RESOLUTION, FINE FEATURES, AND THIN WALLS
The ProJet MJP 2500 Plus 3D printer now offers a high resolution XHD printing mode (1600x900x1600 DPI), developed specifically for high precision applications with VisiJet Crystal. Its durability enables geometries that were previously impossible to reliably produce with wax alternatives. The added durability makes it possible to print extremely thin walls and preserve even the finest, small-scale details, down to 0.1 mm, throughout the manufacturing process.
CASTING QUALITY
Achieve higher quality casting patterns with an optimized printer and material combination that delivers higher resolution, retention of fine details even on small prints, and clean burnout. Even the most delicate patterns with fine features and thin walls are possible with a more durable yet flexible acrylate material. VisiJet Crystal performs well for patterns that require stone-setting. Improve your casting success rate for the most delicate patterns with the durability of 3D printed VisiJet Crystal material.
- Rings, broches, bracelets, mesh features, and more that have highly-detailed, complex geometries, and thin walls
- Prototyping and modeling
HIGH VOLUME PRODUCTION
Fast printing speed, large build volume, advanced software, and batch post-processing maximize your jewelry casting pattern production workflow. 3D print high quality patterns faster for rings, broches, bracelets, necklaces, and many other intricate jewelry pieces. Produce more while eliminating time, cost, and geometric constraints often associated with tooling in traditional jewelry manufacturing processes.
- Castable patterns production for high-volume and mass custom jewelry manufacturing
SIMPLICITY
3D Sprint is a locally installed advanced software used for file preparation, editing, printing and management from a single, intuitive interface. It receives regular updates and significantly decreases the total cost of ownership by reducing the need for costly software seats or subscriptions offered through third party vendors. Features include automated part placement, support generation, and tools to modify pattern geometry without the need to go back to a CAD program. The ProJet Finisher oven offers a batch post-processing turnkey and hands-free support removal solution.
APPLICATIONS
- Larger build area than projector-based printers
- Enables high volume production of patterns for direct casting; no tooling required
BENEFITS
- Builds complex geometries and thin walls not feasible with wax patterns
FEATURES
- Virtually hands-free support removal process
- Clean pattern burnout
- Easy to handle casting patterns
- Biocompatible
VisiJet Crystal in support material
VisiJet Crystal metal casting pattern, no support material
Final gold casted jewelry piece
| PRINTER PROPERTIES | |
|---|---|
| Dimensions(WxDxH) | |
| 3D Printer Crated | 1397 x 927 x 1314 mm(55 x 36.5 x 51.7 in) |
| 3D Printer Uncrated | 1120 x 740 x 1070 mm(44.1 x 29.1 x 42.1 in) |
| Weight | |
| 3D Printer Crated | 325 kg(716 lb) |
| 3D Printer Uncrated | 211 kg(465 lb) |
| Electrical Requirements | 200-240VAC,50/60Hz,单 phase |
| Internal Hard Drive | 500Gb minimum |
| Operating Temperature Range | 25℃(77℉) |
| Operating Humidity | 30-70% relative humidity |
| Noise | <65dBa estimated(at medium fan setting) |
| Certifications | CE |
| MATERIALS | |
|---|---|
| Build Material | VisiJet M2P-CST Crystal |
| Support Material | VisiJet M2 SUP |
| Material Packaging | |
| Build Material | 1.5kg bottles |
| Support Material | 1.4kg bottles |
| Auto Switching Bottle Capacity | 2 of each (build/support) |
MATERIALS
| 3D Sprint® Software | Easy build job set-up, submission and job queue management; Automatic part placement and build optimization tools; Part stacking and nesting capability; Extensive part editing tools; Automatic support generation; Job statistics reporting tools |
|---|---|
| Client Hardware Minimum Specifications | Intel® or AMD® processor with a minimum of 2.0GHz and 4GB RAM; OpenGL 2.1 and GLSL 1.20 enabled graphics card; screen resolution 1280x960; Dedicated Graphics Card: Nvidia GeForce GTX 285, Quadro 1000, AMD Radeon HD 6450, or newer; 10GB of available hard-disk space; additional space may be needed for cache. Temporary file cache requires about 3GB free disk space for every 100 million points. Internet Explorer 9 or newer; Other: 3 button mouse with scroll, keyboard, Microsoft.NET Framework 4.8 installed with application |
| 3D Connect™ Capable | 3D Connect Service provides a secure cloud-based connection to 3D Systems service teams for support. |
| Connectivity | Network ready with 10/100/1000 base ethernet interface; USB port |
| E-mail Notice Capability | Yes |
| Client Operating System | Windows 8.1~Windows 11(64-bit) |
| Input Data File Formats Supported | STL, CTL, OBJ, PLY, ZPR, ZBD, AMF, WRL, 3DS, FBX, IGES, IGS, STEP, STP, MJPDDD |
- DISCLAIMER: It is the responsibility of each customer to determine that its use of any VisiJet material is safe, lawful and technically suitable to the customer’s intended applications. The values presented here are for reference only and may vary. Customers should conduct their own testing to ensure suitability for their intended application.
VisiJet® M2P-CST Crystal
| METRIC | METHOD | METRIC | US |
|---|---|---|---|
| Viscosity(@25C) | Brookfield viscometer | 16cPs | 39lb/ft·h |
| Color | Yellow(Translucent) | ||
| Liquid Density(@25C) | Kruss K11 Force Tensiometer | 1.03g/cm3 | 0.036lb/in3 |
| Default print layer thickness | Internal | 16μm | 0.001in |
| Speed-XHD | Internal | 6.2mm/hr | 0.24in/hr |
SOLID MATERIAL
| METRIC | ASTM METHOD | METRIC | ENGLISH | ISO METHOD | METRIC | ENGLISH |
|---|---|---|---|---|---|---|
| PHYSICAL | PHYSICAL | |||||
| Solid Density | ASTM D792 | 1.19 g/cm3 | 0.043 lb/in3 | ISO 1183 | 1.19 g/cm3 | 0.043 lb/in3 |
| 24 Hour Water Absorption | ASTM D570 | 0.64% | 0.64% | ISO 62 | 0.64% | 0.64% |
| MECHANICAL | MECHANICAL | |||||
| Tensile Strength Ultimate | ASTM D638 Type IV | 28MPa | 4100psi | ISO 527-1/2 | 22MPa | 3100psi |
| Tensile Strength at Yield | ASTM D638 Type IV | 29MPa | 4000psi | ISO 527-1/2 | 20MPa | 2800psi |
| Tensile Modulus | ASTM D638 Type IV | 1300MPa | 190ksi | ISO 527-1/2 | 1000MPa | 150ksi |
| Elongation at Break | ASTM D638 Type IV | 12.9% | 12.9% | ISO 527-1/2 | 10.7% | 10.7% |
| Elongation at Yield | ASTM D638 Type IV | 7.7% | 7.7% | ISO 527-1/2 | 6.9% | 6.9% |
| Flex Strength | ASTM D790 | 31MPa | 4500psi | ISO 178 | 36MPa | 5200psi |
| Flex Modulus | ASTM D790 | 900MPa | 130ksi | ISO 178 | 1300MPa | 188ksi |
| Izod Notched Impact | ASTM D256 | 19J/m | 0.3ft-lb/in | ISO 180-A | 2J/m² | 0.001ft-lb/in² |
| Izod Unnotched Impact | ASTM D4812 | 250J/m | 5ft-lb/in | ISO 180-U | 20J/m² | 0.0087ft-lb/in² |
| Shore Hardness | ASTM D2240 | 75D | 75D | ISO 7619 | 75D | 75D |
| THERMAL | THERMAL | |||||
| Tg(DMA E") | ASTM E1640(E"Peak) | 22℃ | 72℃F | ISO 6721-1/11(E"Peak) | 22℃ | 72℃F |
| HDT 0.455MPa/66PSI | ASTM D648 | 49℃ | 121℃F | ISO 75-1/2B | 49℃ | 121℃F |
| HDT 1.82MPa/264 PSI | ASTM D648 | 42℃ | 108℃F | ISO 75-1/2A | 42℃ | 108℃F |
| CTE -20 TO 50C | ASTM E831 | 105ppm/℃ | 58ppm/℃F | ISO 11359-2 | 105ppm/℃ | 58ppm/℃F |
| CTE 75 TO 180C | ASTM E831 | 175ppm/℃ | 97ppm/℃F | ISO 11359-2 | 175ppm/℃ | 97ppm/℃F |
| Ash Content | ASTM D5630 | 0.026% | 0.026% | ISO 11359-2 | 0.026% | 0.026% |
VisiJet M2P-CST Crystal - ASTM D638 - Representative Curve
Note: Not all products and materials are available in all countries – please consult your local sales representative for availability
2024 by 3D Systems, Inc. All rights reserved. Specifications subject to change without notice. 3D Systems, the 3D Systems logo, ProJet, Visijet and 3D Sprint are registered trademarks of 3D Systems, Inc.
Warranty/Disclaimer: The performance characteristics of these products may vary according to product application, operating conditions, and other factors.