HP MJF PA 12 Data sheet.pdf
HP 3D High Reusability PA 12
Strong, lowest cost,¹ quality parts
Produce strong, functional, detailed complex parts
- Robust thermoplastic produces high-density parts with balanced property profiles and strong structures.
- Provides excellent chemical resistance to oils, greases, aliphatic hydrocarbons, and alkalies.²
- Ideal for complex assemblies, housings, enclosures, and watertight applications.
- Biocompatibility certifications—meets USP Class I-VI and US FDA guidance for Intact Skin Surface Devices.³
Quality at the lowest cost per part¹
- Achieve the lowest cost per part¹ and reduce your total cost of ownership.⁴
- Minimize waste—reuse surplus powder batch after batch and get functional parts, no throwing away anymore.⁵
- Get consistent performance while achieving 80% surplus powder reusability.⁶
- Optimize cost and part quality—cost-efficient material with industry-leading surplus powder reusability.³
Engineered for HP Multi Jet Fusion technology
- Designed for production of functional parts across a variety of industries.
- Provides the best balance between performance and reusability.⁷
- Achieves watertight properties without any additional post-processing.
- Engineered to produce final parts and functional prototypes with fine detail and dimensional accuracy.
Technical specifications
| Category | Measurement | Value | Method |
|---|---|---|---|
| General properties | Powder melting point (DSC) | 18℃/396°F | ASTM D13418 |
| Particle size | 60 µm | ASTM D13451 | |
| Bulk density of powder | 0.12 g/cm³/0.015 lb/in³ | ASTM D13468 | |
| Density of grains | 1.01 g/cm³/0.036 lb/in³ | ASTM D13792 | |
| Mechanical properties | Tensile strength, max load, X*Y | 48 Mpa/6960 psi | ASTM D638 |
| Tensile strength, max load, Z | 48 Mpa/6960 psi | ASTM D638 | |
| Tensile modulus, X*Y | 1800 MPa/261 kips | ASTM D638 | |
| Tensile modulus, Z | 1800 MPa/261 kips | ASTM D638 | |
| Elongation at break, X*Z | 20% | ASTM D638 | |
| Elongation at break, X*Z | 15% | ASTM D638 | |
| Flexural strength @ 5%, X*Y | 65% PMPa/250 psi | ASTM D1790 | |
| Flexural strength @ 5%, Z | 70% PMPa/250 psi | ASTM D1790 | |
| Flexural modulus, X*Y | 1730 PMPa/251 psi | ASTM D1790 | |
| Flexural modulus, Z | 1730 PMPa/251 psi | ASTM D1790 | |
| Lod impact notched @ 3.2 mm, (23°C), YX2 | 3.5 kJ/m² | ASTM D256 Test Method A | |
| Heat deflection temperature @ 0.45 MPa, 66 psi, XY | 175℃/347°F | ASTM D648 Test Method A | |
| Heat deflection temperature @ 1.82 MPa, 264 psi, XY | 95℃/203°F | ASTM D648 Test Method A | |
| Heat deflection temperature @ 1.82 MPa, 264 psi, Z | 95℃/203°F | ASTM D648 Test Method A | |
| Reusability | Refresh ratio for stable performance | 20% | |
| Recommended deuterium humidity | 50 %/70 %H | ||
| Certifications | GSP Class IV and US FDA guidance for Intact Skin Surface Devices, RoHS, EU REACH, PAHs, UL 94, UL 746A |
Ordering Information
| Product | Product number | Weight | Capacity | Dimensions (xyz) | Compatibility |
|---|---|---|---|---|---|
| HP 30 High Reusability PA12 | V1R10A | 13 kg/28.7 lb | 301⁰ | 600 x 333 x 302 mm | HP Jet Fusion 410/420/420 |
| HP 30 High Reusability PA12 | V1R16A | 130 kg/286.7 lb | 3001⁰ | 800 x 600 x 325 mm | HP Jet Fusion 410/420/420 |
| HP 30 High Reusability PA12 | V1R34A | 130 kg/286.7 lb | 3001⁰ | 800 x 600 x 325 mm | HP Jet Fusion 410/420/420 |
| HP 30 High Reusability PA12 | V1R20A | 600 kg/1322.8 lb | 14001⁰ | 1143 x 1143 x 1500 mm | HP Jet Fusion 410/420/420 |
Eco Highlights
- Powders and agents are not classified as hazardous15
- Cleaner, more comfortable workplace—enclosed printing system, and automatic powder management
- Membranes used to indicate leading reusability of powder17
Find out more about our sustainable products at hp.com/resolutions