PA2200_Material_data_sheet_12-08_en.doc
Material Data Sheet
PA 2200
1 General
Typical applications of the material are fully functional parts with high end finish right from the process, which easily withstand high mechanical and thermal load. PA 2200 is suitable for processing on the following systems:
- EOSINT P 730, P 700
- EOSINT P 390, P 385, P 380i, P 380, with or without powder conveying system
- EOSINT P 360 with upgrade S£tP, P 350/2 with upgrade 99 and upgrade S£tP
- FORMIGA P 100
2 Technical Data
General Material Properties
| Property | Value |
|---|---|
| Average grain size (ISO 13320-11) | 56 µm |
| Laser diffraction | 2.20 mil |
| Bulk density (EN ISO 60) | 0.45 g/cm³ |
| Density of laser-sintered part (EOS method) | 0.93 g/cm³ (58 lb/ft³) |
Mechanical Properties
| Property | Value |
|---|---|
| Tensile modulus (EN ISO 527) | 1700 MPa |
| Tensile strength (EN ISO 527) | 48 MPa |
| Elongation at break (EN ISO 527) | 24 % |
| Flexural modulus (EN ISO 178) | 1500 MPa |
| Flexural strength (EN ISO 178) | 58 MPa |
| Charpy – Impact strength (EN ISO 179) | 53 kJ/m² |
| Charpy – Notched impact strength (EN ISO 179) | 4.8 kJ/m² |
| Izod – Impact strength (EN ISO 180) | 32.8 kJ/m² |
| Izod – Notched impact strength (EN ISO 180) | 4.4 kJ/m² |
| Ball indentation hardness (EN ISO 2039) | 78 N/mm² |
| Shore D – hardness (ISO 868) | 75 - |
The mechanical properties depend on the x-, y-, z-position and on the exposure parameters used.
Thermal Properties
| Property | Value |
|---|---|
| Melting point (EN ISO 11357-1) | 172 – 180 °C |
| Vicat softening temperature B/50 (EN ISO 306) | 163 °C |
| Vicat softening temperature A/50 (EN ISO 306) | 181 °C |
The data are based on our latest knowledge and are subject to changes without notice. They do not guarantee properties for a particular part and in a particular application.